1. Longer Life at lower cost
2. High adhesion
3. Cut edge construction
4. Excellent efficiency of Vulcanized splice
5. Complete efficiency of vulcanized splice.
6. Proper loading support
7. Highest resistance to mildewed moisture.
8. Highest resistance to impacted material trapping
| Cover Rubber for General purpose | | | |
| Standard | Grade | Tensile Strength | Tensile strength (kgf/cm2) | | |
| CNS | S | 18 Mpa | 180 | | |
| JIS | S | 18 Mpa | 180 | | |
| RMA | RMA I | 2500 psi | 180 | | |
| RMA II | 2000 psi | 140 | | |
| BS | N17 | 17 Mpa | 180 | | |
| M24 | 24 Mpa | 240 | | |
| DIN | W | 18 N/mm2 | 180 | | |
| X | 25 N/mm2 | 240 | | |
| Y | 20 N/mm2 | 180 | | |
| Z | 15 N/mm2 | 150 | | |
| ISO | H | 24 N/mm2 | 240 | | |
| D | 18 N/mm2 | 180 | | |
| L | 15 N/mm2 | 150 | | |
| AS | N | 18 Mpa | 180 | | |
| M | 24 Mpa | 240 | | |
| | | | | | |
| Tensile strength and number of ply | | | |
| Strength | 2 ply | 3 ply | 4 ply | 5 ply | 6 ply |
| 160 | 160/2 | | | | |
| 200 | 200/2 | | | | |
| 250 | 250/2 | 250/3 | | | |
| 315 | 315/2 | 315/3 | | | |
| 400 | 400/2 | 400/3 | 400/4 | | |
| 500 | | 500/3 | 500/4 | 500/5 | |
| 630 | | 630/3 | 630/4 | 630/5 | 630/6 |
| 800 | | 800/3 | 800/4 | 800/5 | 800/6 |
| 1000 | | 1000/3 | 1000/4 | 1000/5 | 1000/6 |
| 1250 | | | 1250/4 | 1250/5 | 1250/6 |
| 1500 | | | | 1500/5 | 1500/6 |
| 1600 | | | | 1600/5 | 1600/6 |
| 1800 | | | | | 1800/6 |
| 2000 | | | | | 2000/6 |
Taiwan